渣油催化裂化催化剂DYC-01

RFCC Catalyst DYC-01

渣油催化裂化催化剂DYC-01是澳门新莆京7906利用专有DYC催化剂技术平台针对M100、M180、焦化蜡油等劣质催化原料专门开发的一种渣油转化催化剂,该种催化剂具有孔道阶梯分布合理、比表面积大、分子筛活性组分高、稳定性好、抗碱性氮和重金属污染能力强等特点,特别适用于加工劣质催化原料,增加液收。
  RFCC catalyst DYC-01 is specially developed by Shandong Duo You Technology Co. Ltd. with its proprietary DYC technology platform for M100, M180, CGO (coker gas oil) and other heavy feedstocks, featured with graded distribution of pore structures, higher specific area, higher content of zeolite, good hydrothermal stability, benefits on contaminant metals resistance and basic nitrogen poisoning tolerance, particularly applicable for heavy feedstock to enhance yield of valuable products.
1、DYC-01催化剂的物化性能指标
1、Physical-chemical Specification of DYC-01 Catalyst.

表1 DYC-01催化剂的物化性能质量指标
Table 1  Physical-chemical Specification of DYC-01 Catalyst

*催化剂经800oC、100%水蒸气条件下老化;标准轻柴油进料,460℃反应。
*Catalyst steamed under 800oC/100% steam;standard light diesel feed,cracking temperature 460 ℃。

2、抗重金属污染性能
2、Contaminant Metals Resistance

图1  金属污染对DYC-01与对比渣油催化剂活性的影响
Figure 1  Effect of Contaminant Metals Levels of DYC-01 and Competitive RFCC Catalyst


  图1 结果表明,与国内外广泛使用的渣油催化剂相比,DYC-01催化剂在抗重金属污染方面具有明显的优势。
  The results in figure 1 showed that DYC-01 catalyst had significant advantages on contaminant metals resistance compared with widely-used competitive RFCC catalyst.
3、ACE催化裂化性能评价
3. Catalytic Cracking Performance of DYC- 01 Catalyst on ACE Unit
  采用M100作为评价原料,在ACE反应评价装置上对DYC-01催化剂的催化性能进行了评价。表2给出了催化裂化反应评价结果。
  The catalytic performance evaluation of DYC-01 catalyst was carried out with M100 feed in ACE catalytic cracking testing unit. Results are listed in Table 2.
 

表2  ACE催化裂化评价结果
Table 2  Results of DYC-01 Catalyst on ACE Unit

 *催化剂经100%水蒸汽,17小时,800℃老化处理;
*Catalyst steamed at 800℃/100% steam/17h;
  从表2结果可以看出:在相同反应评价条件下,DYC-01催化剂的转化率比对比渣油催化剂高2.09个百分点,焦炭产率相当,汽油+柴油收率和总液收分别提高1.4个百分点,液化气+汽油+柴油收率和总液收分别提高1.85个百分点,油浆下降1.60个百分点。充分显示了DYC-01催化剂优良的渣油催化裂化和抗重金属污染的性能。
  Table 2 shows that under the same reaction conditions, compared with competitive RFCC catalyst, heavy oil conversion for DYC-01 catalyst was higher by 2.09%, gasoline+LCO yield and LPG+gasoline+LCO Yield is higher by 1.24% and 2.05%, respectively, meanwhile, coke yield remains the same, bottoms yield decreases by 1.60%. The results fully show that DYC-01 catalyst has better performance on both resid cracking and contaminant metals tolerance.
  上述结果表明:DYC-01催化剂不仅具有很好的物化性能指标,而且具有很好的催化裂解高金属和高碱性氮含量的劣质渣油的能力。我们相信,选用DYC-01催化剂,必将会提高重油催化裂化装置的经济效益。
  Based on these results, the following observations can be made: DYC-01 catalyst combines good physical-chemical properties with high cracking conversion potential of resid containing high levels of metals and basic nitrogen. We believe that the application of DYC-01 catalyst will definitely enhance economic potential of RFCC unit.

渣油催化裂化催化剂DYC-01 0 本文被阅读 0 次
上一条: 低生焦催化裂化催化剂DYC-LC下一条:高活性重油催化裂化助剂DYC-HAA
   
 

  澳门新莆京7906座落于山东省精细化工循环经济工业园(菏泽市郓城县),园区紧邻京九铁路、京沪高铁、济广高速、日东高速、327省道、京杭大运河和济宁机场,距济南国际机场和郑州国际机场仅2小时路程,水陆空交通便利,敬享得天独厚的经济发展环境。
  澳门新莆京7906成立于2011年,是从事分子筛、炼油催化剂、助剂的研究  >> 详细点击

   
 
       
2019-12-23
2018-7-26
2015-6-19
2015-6-18
2015-6-18
2015-6-18
 
2022-7-29
2022-7-29
2022-2-21
2021-12-28
2021-12-28
2021-12-28
 
 
 
 

澳门新莆京7906 
咨询热线:0530-6860099 传真:0530-6860099  邮箱地址:duoyoukeji@126.com  地址:山东郓城精细化工循环经济工业园
公示信息 鲁ICP备19032961号-1




Baidu
sogou